Sudan NS-160 fiberglass board G10
Category:
SudanGlass fiber board
Product Description
NS-160 series epoxy glass cloth laminated board (G-10)
Product Description:
The NS-160 series epoxy glass cloth laminated board is a plate-like insulation material made by high-temperature pressing of epoxy resin pre impregnated glass cloth The NS-160 series belongs to UL94 HB grade high heat resistant composite materials, which are composite with relevant product specifications such as NEMA G-10, MIL-I-24768/2GEE, and IEC 60893 EPGC201. NS-160G is natural water green, NS-160Y is yellow, NS-160B is black, and NS-160S can also be customized according to customer requirements
Product advantages:
· Has high mechanical strength at high temperatures
· Excellent insulation performance under high humidity
· Excellent electrical performance in ordinary dry environments
· Maximum long-term working temperature 130C
· Excellent heat resistance, insulation level B
· Meets UL94 HB flame retardant standard
· High cost-effectiveness of the product
Product application:
Industrial machinery, machine components, electrical wires, mechanical wires, bearings, gaskets, gears, washers, computer electronic equipment, carriers, electrical boards, circuit board fixing parts, wave soldering brackets, fins, converters, wiring boards, heterosexual parts, transformers, wear-resistant bars, etc
Product specifications
Metric:
·Thickness: 0.1mm~100mm or customized by the customer
·Thickness: 0.004 "~4" (NEMA standard thickness) or customized by the customer. Dimensions: 40 "x48", 48 "'x96", up to 48 "x120"
English:
·Thickness: 0.004 "~4" (NEMA standard thickness) or customized by the customer
·Dimensions: 40 "x48", 48 "'x96", maximum up to 48 "x120"
| Product parameters | ||||
| Test items | Test conditions | Unit | Typical value | |
| Voltage withstand strength | Z-direction | C-90/20/65 15 | KV/mm | 54 |
| X. Y-direction | 0-0.5/90 | KV | 28 | |
| insulation resistance | Original sample | C-90/20/65 | MΩ | 10⁶-10⁸ |
| After cooking | C-90/20/65+D-2/ 100 | MΩ | 10⁴-10⁶ | |
| Volumetric resistance | C-96/35/90 | MΩ-cm | 10⁷-10⁹ | |
| Surface resistance | C-96/35/90 | MΩ | 10⁶-10⁸ | |
| Dielectric constant (1MHz) | Fluid cell | 4.2-4.7 | ||
| Dielectric loss (1MHz) | Fluid cell | 0.030-0.035 | ||
| Arc resistance | ASTM D495 | Sec | 120-140 | |
| Leakage trace index | ASTM D3638 | V | 175-250 | |
| bending strength | Y -Direction | ASTM D790 | MPa | 400-500 |
| X-Direction | MPa | 450-550 | ||
| compressive strength | Y-Direction | ASTM D695 | MPa | 350-440 |
| X-Direction | MPa | 290-390 | ||
| tensile strength | ASM D882 | MPa | 250-350 | |
| Bending modulus | ASTM D790 | MPa | 21560-24500 | |
| Interlayer bonding force | D-48/50 | kN | 8.0-10.0 | |
| Rockwell hardness | ASTM D785 | HR-R A | 120-125 | |
| Notch impact strength | X-axis | ASTM D256 | J/cm | 5.4-6.4 |
| Glass transition temperature | DSC | IPC-TM-650 2.4.25 | C | 135 |
| Water absorption | 1.0mm thickness | E-24/50+D-24/23 | % | 0. 1-0.8 |
| proportion | As received | g/cm3 | 2.0±0.15 | |
| Coefficient of thermal expansion | X,Y-Direction | RT〜200C | PPM/C | 11-14 |
| Z -Direction | RT〜135C | PPM/C | 45-50 | |
| 135-2OOC | PPM/C | 250-260 | ||
| Flame retardancy | UL94 | Rating | HB | |
| Relative Temperature Index (RTI) | UL94 | C | 130 | |
| Heat resistance | 130C/2Hr | pass | ||
| 280C/30S | Pass | |||
| Insulation level | IEC 60216- 1 | Class | B | |
| Note: The above test data are typical test values and are not guaranteed specification values | ||||
| Characteristics & Applications | For template test PCB & ICT applications. | ||
| Colour | Green | ||
| Standard Sheet Size (mm) | 1020*1220 | ||
| Specific Gravity (g/cm 3) | 2.1~2.15 | ||
| Volume Resistivity M Q *cm | C-96/35/90 ≥1.0X10⁶ | ||
| Volume Resistivity M Q *cm | 150℃ ≥1.0x10⁴ | ||
| Surface Resistivity MQ | C-96/35/90 ≥l.OxlO⁴ | ||
| Surface Resistivity MQ | 150℃ | ≥l.OxlO⁴ | |
| Resistance S | D-48/50+D-0.5/23 ≥60 | ||
| Dielectric breakdown KV | D-48/50+D-0.5/23 ≥40 | ||
| Dielectric constant( 1 MHz) | ≤5.4 | ||
| Dielectri Factorf l MHz) | 1MHzC-24/23/50 <0.035 | ||
| Water Absorption | E-1/105+D-24/23 ≤0.8% | ||
| Insulation Resistance | C-90/20/66 | 10¹⁰~10¹⁴Ω | |
| FlexuralStrength | LW | A ≥415 N/mm2 | |
| CW | A ≥345 N/mm2 | ||
| Comparative Tracking Index V | IEC60112 | ≥175 | |
| Thermal Stress | Unetched Etched | 160℃,10S/solderdip No delamination | |
Subscribe
If you have any questions about our products or price list, please contact us and we will contact you within 24 hours.
Scan Follow Consultation
Tel: +86-400 616 0980
Phone: +86 13826920244 Miss Yang
+86 13903032405 Mr. Yi
Hunan Company: Noves New Materials Industrial Park, No. 5 Shengyuan Road, Yueyang High tech Industrial Park
Jiangsu Company: No. 29 Heshun Road, Industrial Park, Suzhou City, Jiangsu Province
Dongguan Company: No. 2 Xingguang Xinglang Road, Huangjiang Town, Dongguan City, Guangdong Province/No. 2 R&D Fifth Road, Songshan Lake Park
Privacy policy SEO DigitalCard Support: 300.cn Dongguan